物理性能
各温度°C时弹性模量 | 20°C与各温度间热膨胀系数 | 热导率 | 比热容 | 电阻率 | 磁性 |
20 | 100 | 200 | 300 | 400 | 500 | 100°C | 200°C | 300°C | 400°C | 500°C | 20°C | 20°C | 20°C |
GPa | 10-6K-1 | W/m.K | J/kg.K | Ω.mm2/m |
195 | 190 | 182 | 174 | 166 | 158 | 15.8 | 16.1 | 16.5 | 16.9 | 17.3 | 12 | 450 | 1 | no* |
*-Small amounts of ferrite and/or martensite caused by cold deformation will increase the magnetizability. (由冷变形产生的少量铁素体和/或马氏体将提高磁化率.)